Recommended Process Condition:

Laminate Temperature：120～140℃
Pressure：10Mpa
Duration time：20-25minute
The processing conditions are for the reference only.
The parameter should be adjusted base on spot condition.

Use and characteristic:

The products, which have the features of good temperature resistance, good anticorrobility and long durability, are widely used in PVC magnetic cards based on which telecom card, identification card. transaction cards, attendance cards and dining card. The products are suitable for laminating techniques.

General Characteristics
Base film material: Polyester
Magnetic layer material: Ferrite
Color: Black
Thickness Characteristics
Base film thickness：（12±1）µm
Total thickness：（26~29）µm
Magnetic Characteristics
Coercivity Hc：28.7kA/m（360 Oe）
Retentivity Br：1.4±0.14（10-6 Wb/m）
Squareness K：≥0.8

Signal Amplitude Characteristics

Signal amplitude UA1：80~130% UR
Signal amplitude Ui1：≤136% UR
Signal amplitude UA2：≥80% UR
Signal amplitude Ui2：≥65% UA2
ResolutionUA3：≥70% UA2
Erasure UA4：≤3% UR
Extra pulse Ui4：≤5% UR

Wear Resistance Characteristics

According to ISO/IEC 7811-2/10373
Average signal amplitude: UA after≥60% UAbefore
Individual signal amplitude：Ui after≥80% Uibefore
Durability：≥2000 times

Chemical Resistance Characteristics

According to ISO/IEC 7811-2/10373
Average signal amplitude：UAafter≥90% UAbefore
Individual signal amplitude：Uiafter≥90% Uibefore

Storage Conditions：

The allowed storage period for the reel is 3 years at
temperature 10~30℃，humidity 40%~60%RH，Heavy pressing strictly prohibited.
Not more than 6 boxes pile up, far away from the magnetic field.
Handle with care, avoid fierce vibration, and keep off sun and rain, far away from magnetic field in the transportations.